1.7383 11CrMo9-10 Forged Forging Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products
parameters1：
parameters2：
parameters3：
We are professional 1.7383 11CrMo9-10 Forged Forging Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products from china.
Chemical composition % of steel 11CrMo9-10 (1.7383): EN 10222-2-2000| C | Si | Mn | P | S | Cr | Mo |
| 0.08 - 0.15 | max 0.5 | 0.4 - 0.8 | max 0.025 | max 0.015 | 2 - 2.5 | 0.9 - 1.1 |
Mechanical properties of steel 11CrMo9-10 (1.7383)
|
| Rm - Tensile strength (MPa) (+QT) | 540-680 |
| Nominal thickness (mm): | to 200 | 200 - 500 |
|
| Rm - Tensile strength (MPa) (+NT) | 520-670 | 450-600 |
|
| Rm - Tensile strength (MPa) (+QL) | 520-670 |
|
| ReH - Minimum yield strength (MPa) (+QT) | 355 |
| Nominal thickness (mm): | to 200 | 200 - 500 |
|
| ReH - Minimum yield strength (MPa) (+NT) | 310 | 265 |
|
| ReH - Minimum yield strength (MPa) (+QL) | 310 |
|
| KV - Impact energy (J) transverse, | +20°
27-50 |
|
| KV - Impact energy (J) longitud., | +20°
40-60 |
| Nominal thickness (mm): | to 200 | 200 - 500 |
|
| A - Min. elongation at fracture (%) longitud., (+NT) | 20 | 23 |
| Nominal thickness (mm): | to 200 | 200 - 500 |
|
| A - Min. elongation at fracture (%) transverse, (+NT) | 20 | 21 |
| Nominal thickness (mm): | to 60 | 60 - 100 |
|
| A - Min. elongation at fracture (%) (+QL) | 18 | 17 |