1.4432 X2CrNiMo17-12-3 X2CrNiMo17.12.3 Forged Forging Round Bars Hollow Bars Shafts Square rectangular rectangle Blocks Discs Disks Plates Flat Bars
parameters1:
parameters2:
parameters3:
We are professional 1.4432 X2CrNiMo17-12-3 X2CrNiMo17.12.3 Forged Forging Round Bars Hollow Bars Shafts Square rectangular rectangle Blocks Discs Disks Plates Flat Bars from china
Chemical composition % of steel X2CrNiMo17-12-3 (1.4432): EN 10088-2-2005Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
C | Si | Mn | Ni | P | S | Cr | Mo | N |
max 0.03 | max 1 | max 2 | 10.5 - 13 | max 0.045 | max 0.015 | 16.5 - 18.5 | 2.5 - 3 | max 0.11 |
Mechanical properties of steel X2CrNiMo17-12-3 (1.4432)
|
Rm - Tensile strength (MPa) (+A) | 490-700 |
|
Rm - Tensile strength (MPa) (+AT) | 490-690 |
|
Rm - Tensile strength (MPa) (+AT+C) | 750-780 |
|
Rp0.2 0.2% proof strength (MPa) (+A) | 190-240 |
|
Rp0.2 0.2% proof strength (MPa) (+AT) | 190 |
|
KV - Impact energy (J) transverse, (+A) | +20° 60 | -196° 60 |
|
KV - Impact energy (J) longitud., (+A) | +20° 100 |
|
A - Min. elongation at fracture (%) (+A) | 40-45 |
|
A - Min. elongation at fracture (%) longitud., (+AT) | 40 |
Nominal diameter (mm): | 2 - 50 |
|
Z - Reduction in cross section on fracture (%) | 63-68 |
Brinell hardness (HB): (+A) | 215 |
Brinell hardness (HB): (+AT) | 200 |
Properties of steel X2CrNiMo17-12-3 (1.4432)Resistance to intergranular corrosion: in the delivery condition - yes; in the sensitized condition - yes Steel shal not be applied at a metal temperature lower than -196 ° C |